Акриловый модификатор ударопрочности AIM 6100TP
Acrylic Impact Modifier
Acrylic Impact Modifier for Transparent product:AIM6100TP
Part 1: Introduction
Revision date: 1st July,2017
AIM 6100TP is acrylic impact modifier with core/shell structure in which core being moderate cross linked structure is linked with shell by grafting copolymerization. It not only improves impact resistance performance of the product, but also increases the surface gloss, especially PVC outdoor transparent products.
Part 2: Advantages
Promote fusion
Excellent weatherability
Outstanding surface quality
Improve impact-strength with no influence of transparent
Part 3: Application
AIM 6100TP can be used in outdoor transparent products, such as corrugated sheets, sign boards, building materials and sheets and films.
Part 4: Technical specifications
|
Specification |
Unit |
Test standard |
AIM 6100TP |
|
Appearance |
-- |
-- |
White powder |
|
Bulk density |
g/cm3 |
GB/T 1636-2008 |
0.45±0.10 |
|
Sieve residue (30 mesh) |
% |
GB/T 2916 |
≤2.0 |
|
Volatile content |
% |
ASTM D5668 |
≤1.3 |
Part 5: Performance Comparison
5.1Formulation for following tests
Mixing equipment type: SHR-5A from Zhang Jiagang Beier Machinery Co., Ltd Mixing condition:110℃ Volume: 5.0
|
Ingredients |
1# W-300 |
2# AIM 6100TP |
|
PVC (K-57) |
100.00 |
100.00 |
|
LubricantG-60 |
1.00 |
1.00 |
|
Lubricant W-165 |
0.50 |
0.50 |
|
Tin stabilizer |
0.80 |
0.80 |
|
Processing aid AIP 5510 |
1.00 |
1.00 |
|
W-300 |
6.00 |
-- |
|
AIM 6100TP |
-- |
6.00 |
5.2Fusion properties comparison
Test equipment type: RM-200C torque rheometer from Harbin Hapro Electrical technology Co., LtdVolume: 60ml
|
Test conditions |
60rpm@190℃ |
||||
|
|
|||||
|
Fusion data Type |
Lowest torque (Nm) |
Highest torque (Nm) |
Equilibrium torque (Nm) |
Fusion time (S) |
|
|
1# W-300 |
11.5 |
27.2 |
11.5 |
21 |
|
|
2#AIM 6100TP |
11.8 |
27.8 |
11.7 |
22 |
|
5.3Optical properties comparison
Test method:
Make sheet with compound on double-roller mill under 185℃ for 5min.
According to the following test standards and test conditions, prepare samples and obtain test results.
|
Type |
Test standard |
Transmittance (%) |
Haze (%) |
|
1# W-300 |
GB/T 2410 |
88.6±0.6 |
4.62±0.04 |
|
2# AIM 6100TP |
GB/T 2410 |
89.3±0.6 |
4.59±0.03 |
5.4Impact strength comparison
Test method:
1.Make plate with compound on double-roller mill under 185℃ for 5min.
2.Then retain 6 min in curing press at 185℃
3.According to the following test standards and test conditions, prepare samples and obtain test results.
|
Item Specification |
Unit |
Test standard |
1# W-300 |
2# AIM 6100TP |
|
Impact strength |
KJ/m2 |
GB/T 1043.1-2008 |
15.2±0.3 |
15.7±0.4 |
Part 6: Packing, transportation and storage
20kg/25 kg bag, 250kg/500 kg super sack
This material is non-dangerous goods for land, air and marine transportation.
Material should be kept from flames, hot pipes, heaters or other sources of heat. Adequate precautions should be taken to keep all dust levels below values that are hazardous to health and safety. The recommended maximum storage temperature for this material is 45 deg.C.
Part 7: Safe Handling
Please consult the MSDS before handling for additional information concerning personal protective equipment, Safety, Health and Environmental information, and always exercise the utmost care in handling.
Общеупотребительные названия продукта: Модификатор ударопрочности, модификатор удара